Introduction
H-13 steel is an air hardening chromium die steel - can be used for a range of applications. The higher vanadium content ensures increased resistance to heat checking and all round improvement to properties at elevated temperatures. We are a trusted H-13 steel supplier, providing high-quality, heat-resistant steel for your industrial needs.
Steel Properties : High hot-wear resistance, high hot tensile strength and toughness. Good thermal conductivity and insusceptibility to hot cracking. Can be water-cooled to a limited extent.
Applications : Hot-work tool steel for universal use. Pressure casting dies and metal extrusion tools for processing light metals, forging dies, moulds, screws and barrels for plastic processing, nitrided ejectors, hot-shear blades. Suitable for Aluminium Extrusion Die & Aluminium Copper Forging Dies.
H13 steel has high hard resistance and hardness.
Suitable for Aluminium Extrusion Die, and Aluminium Copper forging Die.
Chemical Composition : (%)
| C | Si | Mn | Cr |
| 0.37-0.43 | 0.90-1.20 | 0.30-0.50 | 4.80-5.50 |
| Mo | Ni | V | P | S |
| 1.20-1.50 | - | 0.90-1.10 | 0.00-0.030 | 0.00-0.030 |
Grades Equivalent :
STANDARD |
BRAZIL |
AUSTRIA |
EN |
1.2344 |
VM13IM |
W302 |
X40CrMoV5-1 |
SLOVANIA |
ITALY |
JIS |
S.KOREA |
UTOP M02-EFS |
ESKY0S2 |
SKD61 |
STD61 |
TAIWAN |
CZECH REP. |
CHINA |
AMERICA |
GMH13 |
TLIEFS |
YTR5 |
H-13 |
Production Process :
| UT Standard : | Reduction Ratio : | Delivery Status : |
| SEP 1921, (DEC.84)E/e | As 1:4 or 1:5 | In annealed condition. |
Sizes of Round Bars :
Cold Drawn/Ground Bar |
Hot Rolled Annealed Peeled Bar |
Forged Anealed Turned Bar |
Φ 2.0 - 14.4mm |
Φ 14.5 - 80.0mm |
Φ 81.0 - 810.0mm |
Sizes of Hot Rolled Flat Bars/Sand Blasted Machined Straight :
Thickness |
Width |
5mm - 410mm |
10mm - 810mm |
Heat Treatments :
Quenching temperature : 1020-1050℃
Cooling Medium : air-cooling
Tempering temperature : 550-650℃
Tempering times : 2Times, the tempering temperature in the second time should be lower than in first time
Tempering Hardness : 47-48HRC.
Tempering°C |
500°C |
550°C |
600°C |
HRC |
HRC56 |
HRC54 |
HRC50 |