M-2

Steel Properties : For all metal-cutting tools for roughing or finishing, such as twist drills, all kinds of milling cutters, screw taps, screw dies, broaches, reamers, countersinks, thread chasers, segments for circular saws, shaping tools and woodworking tools. Also highly suitable for cold-forming tools, such as cold extrusion rams and dies, as well as cutting and precision cutting tools, plastic moulds with elevated wear resistance and screws.

Applications : Standard high-speed steel grade. High toughness and good cutting power owing to its well-balanced alloy composition; thus suitable for a wide variety of applications.

It is a typical steel grade of W-Mo current hss, with high toughness, good thermal plasticity, high hardness, as well as red hardness and hot hardness.

TGM2 is suitable for producing high quality cutting tools, such as hob, knife, and milling cutter. TGM2A is suitable for producing common cutting tools with high toughness, also suitable for cold-forming tools. M2 steel is suitable for producing common tools.

Sizes of Round Bars :

Sizes of Flat Bars :

Sizes of Square Bars :

Sizes of Sheets :

Heat Treatments :

Annealing :

Annealing temperature : 860-880℃, keep this temperature by 2-4 hours, then cooling to 600℃ in the speed of less than 30℃/h.

If after cold drawn process, suggest and stress relieving annealing process Under the temperature of 600-700℃, keep this temperature by 2 hours.

Quenching & Tempering (salt bath)

Quenching :

Pre-heating in two steps :

Heating temperature under: 400-500℃ and 850-900℃

Austenitizing temperature: 1185-1225℃

Heating coefficient 10-15sec/mm, quenching under 580-620℃, then cooling to room temperature.

Tempering :

Tempering temperature under:540-560℃, tempering 3 times, each time 1 hour, then cooling to room temperature.